1.2mm Acrylic Mirror

Acrylic mirror is more than 10 times stronger than glass mirror.
With more than 30 color available.
With large stock, daily output more than 5000pcs.
Small size free sample available for testing.
Thickness range from 0.85mm to 6mm
Factory direct sale price, able to offer the lowest price in China.

Product Details

mirror application.JPG Mirrored acrylic sheet is made from clear acrylic sheet and colored acrylic sheet with electroplate processing to get the mirror finish. The front surfece with mirror reflecting effect with protection film and back side with painting to protect the mirror. Mirrored acrylic sheet is weather proof, non-toxic, shatter-resistant, and chemical resistance. Its with all features that regular acrylic sheet have.

Acrylic mirror is more than 10 times stronger than glass mirror.

And we have more than 30 color available.

With large stock, daily output more than 5000pcs.

Small size free sample available for testing.

Thickness range from 0.85mm to 6mm

Factory direct sale price, able to offer the lowest price in China.

1.2mm acrylic mirror sheet.jpg

The plexiglass mirror can be mirroed acrylic sheet, PS sheet, PVC sheet and PC sheet etc. It is flexiable and flat surface. The most important more than 10 times stronger than the regular glass mirror. Thickness range from 0.85mm to 6mm, with more than 30 color available.
Standard size 1220x2440 (4ft x 8ft) 1220x1830 (4ft x 6ft)

Custom cut to size and design available

Using

Uising of Mirrored Plexiglass Sheet.jpg

Physical Properties of Acrylic Mirror Sheet

Property	Property	ASTM Typical Value 3 Method mm (Thickness)
Property	Property	ASTM Typical Value 3 Method mm (Thickness)
Acrylic mirror sheet Mechanical Property	Specific Gravity	D792 1.19
	Tensile Strength	D638 700 kg/cm2
	Flexural Strength	D790 1170 kg/cm2
	Modulus of Elasticity	28000-35000 kg/cm2
	Compressive Strength	D695 1200 kg/cm2
	Rockwell Hardness	D785 M-100
Optical Property	Refractive Index	D542 1.49
Optical Property	Light Transmission	D1003 93%
Property	Forming Temperature	Approx 150-180℃
	Deflection Temperature	D648 95℃
	Vicat Softening Point	D1525 120℃ (223℉)
	Coefficient of Linear Thermal Expansion (-18℃ To 38℃ Ave)	D696 5×10-5 cm/cm/℃
	Coefficient of Thermal Conductivity	Cenco-Fitch 6×10-5 cm/cm/℃
	Selflgnition Temperature	D1929 443℃
	Specific Heat	0.35 (BTU/1b℉)
Electrical Property	Volume Resistivity	D257 1016ohm-cm
Electrical Property	Surface Resistivity	D257 1015ohm-cm
Water Absorption	Water Absorption	D570 0.3